RESUMEN
Fe(II)-induced phase transformations of secondary iron minerals have attracted considerable attention due to their influence on antimony (Sb) mobility. However, Fe(II)-induced natural multicomponent secondary iron mineral (nmSIM) transformations and the corresponding repartitioning of Sb on nmSIM under acidic conditions upon Fe(II) exposure have not been systematically examined. Herein, we investigated the effect of Fe(II) on nmSIM mineralogy and Sb mobility in Sb(V)-bearing nmSIM at pH 3.8 and 5.6 at various Fe(II) concentrations over 15 d. The Sb(V)-bearing nmSIM phase transformation occurred under both strongly and weakly acidic conditions without Fe(II) exposure, while the presence of Fe(II) significantly intensified the transformation, and substantial amounts of intermediary minerals, including jarosite, ferrihydrite, lepidocrocite and fougerite, formed during the initial reaction stage, especially at pH 5.6. X-ray diffraction (XRD) analyses confirmed that goethite and hematite were the primary final-stage transformation products of Sb(V)-bearing nmSIM, regardless of Fe(II) exposure. Throughout the Sb(V)-bearing nmSIM transformation at pH 3.8, Sb release was inversely related to the Fe(II) concentration in the initial stage, and after maximum release was achieved, Sb was gradually repartitioned onto the nmSIM. No Sb repartitioning occurred in the absence of Fe(II) at pH 5.6, but the introduction of Fe(II) suppressed Sb release and improved Sb repartitioning on nmSIM. This transformation was conducive to Sb reimmobilization on Sb(V)-bearing nmSIM due to the structural incorporation of Sb into the highly crystalline goethite and hematite generated by the Sb(V)-bearing nmSIM transformation, and no reduction of Sb(V) occurred. These results imply that Fe(II) can trigger mineralogical changes in Sb(V)-bearing nmSIM and have important impacts on Sb partitioning under acidic conditions. These new insights are essential for assessing the mobility and availability of Sb in acid mine drainage areas.